Description
ABS flame retardant compound. Also available UV stabilized.
This grade is also available as an antimicrobial grade which contains a biocide based on silver ion technology
Availability
Africa-Middle East, Asia-Pacific, Europe, Latin America, North America
Typical Properties
Melt Flow Rate (220 °C/10.0 kg)
40 g/10 min
Density (Method A)
1.20 g/cm³
Tensile Modulus (1 mm/min, Type 1A)
2200 MPa
Tensile Stress at Yield (Type 1A, 50 mm/min)
46.0 MPa
Tensile Strain at Yield (Type 1A, 50 mm/min)
2.5 %
Flexural Stress (2.0 mm/min)
70.0 MPa
Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A)
16 kJ/m²
Charpy Impact Strength - Notched (-20 °C, Type 1, Edgewise, Notch A)
5.0 kJ/m²
Notched Izod Impact Strength (Notch A)
15 kJ/m²
Ball Indentation Hardness (H 358/30)
89.0 MPa
Ball Pressure Test (85 °C)
Pass
Vicat Softening Temperature (B (50N), 50 °C/h)
96.0 °C
Deflection Temperature Under Load Unannealed (0.45 MPa) (Flatwise)
93.0 °C
Deflection Temperature Under Load Unannealed (1.80 MPa) (Flatwise)
85.0 °C
Comparative Tracking Index (CTI) (Solution B)
>600 V
Glow Wire Flammability Index (1.0 mm)
960 °C
Glow Wire Ignition Temperature (1.5 mm)
750 °C
Glow Wire Ignition Temperature (3.0 mm)
750 °C
Glow Wire Ignition Temperature (1.0 mm)
725 °C
Flammability Classification (1.0 mm)
V-0
Flammability Classification (1.5 mm)
V-0
Flammability Classification (3.0 mm)
V-0
Flammability Classification (3.0 mm)
5VA