SCHULADUR A3 GF30 LM BKR968112
Description
PBT/ASA 30% Glass Fiber, low warpage
Availability
Europe
Product data and technical information
Typical Properties
Density (Method A)
1.42 g/cm³
Tensile Modulus (23 °C, 1 mm/min, Type 1A)
10500 MPa
Tensile Stress at Break (Type 1A, 23 °C, 5 mm/min)
115 MPa
Tensile Strain at Break (Type 1A, 23 °C, 5 mm/min)
2.0 %
Flexural Stress (2.0 mm/min, 2.5%)
205 MPa
Charpy Impact Strength - Notched (23 °C)
7.0 kJ/m²
Charpy Impact Strength - Notched (-30 °C)
7.0 kJ/m²
Charpy Impact Strength - Unnotched (-30 °C)
48 kJ/m²
Charpy Impact Strength - Unnotched (23 °C)
50 kJ/m²
Vicat Softening Temperature (A (10N), 50 °C/h)
210 °C
Vicat Softening Temperature (B (50N), 50 °C/h)
140 °C
Drying Time
2 to 4 hr
Drying Temperature
100 °C
Processing (Melt) Temp
250 to 260 °C
Mold Temperature
60 to 90 °C