Typical Properties
Melt Flow Rate (300 °C/1.2 kg)
5.4 g/10 min
Melt Flow Rate (300 °C/3.8 kg)
27 g/10 min
Melt Flow Rate (300 °C/5.0 kg)
30 g/10 min
Density - Specific Gravity
1.43 g/cm³
Tensile Modulus (5.0 mm/min, 23 °C, 3.11 mm, Injection Molded)
440 MPa
Tensile Strength at Break (5.0 mm/min, 23 °C, 3.11 mm, Injection Molded)
117 MPa
Flexural Modulus (1.3 mm/min, 1% Secant)
7790 MPa
Flexural Strength at Yield (1.3 mm/min)
118 MPa
Tensile Elongation at Break (5.0 mm/min, 23 °C, 3.11 mm, Injection Molded)
2.7 %
Unnotched Izod Impact (23 °C, 3.08 mm)
930 J/m
Notched Izod Impact (23 °C, 3.07 mm)
180 J/m
Deflection Temperature Under Load Unannealed (264 psi) (12.6 mm)
142 °C
Deflection Temperature Under Load Unannealed (66 psi) (12.6 mm)
146 °C
Coefficent of Linear Thermal Expansion (CLTE), Flow (-20 to 130 °C)
1.8E-5 cm/cm/°C
Coefficent of Linear Thermal Expansion (CLTE), Perpendicular (-20 to 130 °C)
6.5E-5 cm/cm/°C
Burning Rate (2.00 mm)
<100 mm/min
Burning Rate (2.00 mm)
<100 mm/min
Drying Time
3.0 to 6.0 hr
Drying Temperature
121 °C
Nozzle Temperature
304 to 338 °C
Processing (Melt) Temp
316 to 343 °C
Front Temperature
304 to 338 °C
Middle Temperature
293 to 316 °C
Rear Temperature
282 to 304 °C
Mold Temperature
82 to 116 °C
Drying Time, Maximum
6 hr