1031850CT PC E-12672G C3 GRYGRY
Description
PBT
Availability
North America
Product data and technical information
Typical Properties
Melt Flow Rate (260 °C/2.16 kg, Procedure A)
10 g/10 min
Density - Specific Gravity
1.19 g/cm³
Tensile Modulus (50 mm/min)
1960 MPa
Tensile Strength at Yield (50 mm/min)
52.0 MPa
Tensile Strength at Break (50 mm/min)
0.827 MPa
Flexural Modulus (1.3 mm/min)
2130 MPa
Notched Izod Impact
660 J/m
Vicat Softening Temperature
145 °C
Deflection Temperature Under Load Unannealed (66 psi)
130 °C
Drying Time
2.0 to 4.0 hr
Drying Temperature (Desiccant Dryer)
120 to 140 °C
Nozzle Temperature
235 to 255 °C
Processing (Melt) Temp
220 to 270 °C
Front Temperature
225 to 240 °C
Middle Temperature
225 to 240 °C
Rear Temperature
220 to 235 °C
Mold Temperature
<80 °C