12N4006NCBLK
Description
Medium Flow, High Impact, Flame Retardant Polypropylene
Availability
North America
Product data and technical information
Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
6.5 g/10 min
Density - Specific Gravity
0.938 g/cm³
Tensile Strength at Yield
20.7 MPa
Flexural Modulus (Tangent)
1030 MPa
Notched Izod Impact
No Break J/m
Deflection Temperature Under Load Unannealed (66 psi)
82.2 °C
RTI Elec (1.5 to 3.0 mm)
115 °C
RTI Imp (1.5 to 3.0 mm)
115 °C
RTI Str (1.5 to 3.0 mm)
115 °C
Drying Temperature
82 °C
Drying Time
4 hr
Rear Temperature
177 to 216 °C
Middle Temperature
177 to 227 °C
Front Temperature
177 to 227 °C
Nozzle Temperature
177 to 227 °C
Processing (Melt) Temp
182 to 227 °C
Mold Temperature
32 to 66 °C
Back Pressure
<0.689 MPa
Injection Rate
Slow-Moderate
Cushion
6.35 to 12.7 mm
Flame Rating (1.5 mm)
V-2
Flame Rating (3.0 mm)
V-2
UL File Number
E51193