Moplen RP399T
Description
Moplen RP399T is a random copolymer primarily designed for injection molding applications. The grade is nucleated and contains antistatic additives. Moplen RP399T features high melt flow characteristics and is typically used in thin‑walled packaging applications where good transparency and organoleptic properties are required.
Availability
Africa-Middle East, Europe
Product data and technical information
Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
40 g/10 min
Density (23 °C)
0.90 g/cm³
Flexural Modulus
1100 MPa
Tensile Modulus
1000 MPa
Tensile Stress at Yield
29 MPa
Tensile Strain at Break
>50 %
Tensile Strain at Yield
12 %
Notched Izod Impact Strength (23 °C)
5.4 kJ/m²
Vicat Softening Temperature (A50)
125 °C
Heat Deflection Temperature B (0.45 MPa, Unannealed)
73 °C
Haze (1 mm - injection molded disc)
9 %