ABS 3001MC KO500BLK
Description
Diamond ABS 3001MC KO500BLK is a Acrylonitrile Butadiene Styrene material. Features include: Platable.
Availability
North America
Product data and technical information
Typical Properties
Melt Flow Rate (200 °C/5.0 kg, Procedure A)
2.0 g/10 min
Melt Flow Rate (230 °C/3.8 kg, Procedure A)
7.5 g/10 min
Density - Specific Gravity
1.05 g/cm³
Tensile Strength at Yield (51 mm/min)
43.4 MPa
Flexural Modulus (1.3 mm/min, Tangent)
2280 MPa
Notched Izod Impact (23 °C, 3.18 mm)
350 J/m
Rockwell Hardness (R-Scale)
101
Vicat Softening Temperature (Loading 1 (10 N))
103 °C
Deflection Temperature Under Load Annealed (264 psi)
87.2 °C
Deflection Temperature Under Load Unannealed (264 psi) (3.18 mm)
77.8 °C
Drying Temperature
80 to 85 °C
Drying Time
2.0 to 4.0 hr
Suggested Max Moisture
0.1 %
Rear Temperature
190 to 250 °C
Middle Temperature
190 to 250 °C
Front Temperature
190 to 250 °C
Mold Temperature
40 to 80 °C
Injection Rate
Moderate-Fast
Flame Rating (1.5 mm)
HB
UL File Number
E150937