Typical Properties
Density
1.14 g/cm³
Density - Specific Gravity
1.14 g/cm³
Change in Volume (in Reference Fuel B, 27 °C, 168 hr)
25 %
Change in Volume (in Reference Fuel B, 27 °C, 168 hr)
25 %
Change in Volume (in ASTM #1 Oil, 100 °C, 168 hr)
-17 %
Change in Volume (in ASTM #1 Oil, 100 °C, 168 hr)
-17 %
Change in Volume (in IRM 903 Oil, 100 °C, 168 hr)
19 %
Change in Volume (in IRM 903 Oil, 100 °C, 168 hr)
19 %
Change in Volume (in Water, 100 °C, 168 hr)
6.0 %
Change in Volume (in Water, 100 °C, 168 hr)
6.0 %
Melt Viscosity (190 °C, 300 sec^-1)
410 Pa·s
Tensile Stress at 100% (1.90 mm)
4.20 MPa
Tensile Stress at 100% (1.90 mm)
4.20 MPa
Tensile Stress at 100% (125 °C, 1.90 mm)
4.40 MPa
Tensile Stress at 100% (125 °C, 1.90 mm)
4.40 MPa
Tensile Stress at Yield (1.90 mm)
8.70 MPa
Tensile Stress at Yield (125 °C, 1.90 mm)
8.40 MPa
Tensile Strength at Yield (1.90 mm)
8.70 MPa
Tensile Strength at Yield (125 °C, 1.90 mm)
8.40 MPa
Tensile Strain at Break (1.90 mm)
320 %
Tensile Strain at Break (125 °C, 1.90 mm)
280 %
Torsion Modulus (24 °C, 1.9 mm)
2.3 MPa
Torsion Modulus (-20 °C, 1.9 mm)
10.2 MPa
Tensile Set
9 %
Clash-Berg Modulus (-40 °C)
68.9 MPa
Tensile Elongation at Break (125 °C, 1.90 mm)
280 %
Tensile Elongation at Break (1.90 mm)
320 %
Tear Strength (Die C, 1.90 mm)
28.0 kN/m
Ductile/Brittle Transition Temperature
-79 °C
Ductile/Brittle Transition Temperature
-79 °C
Change in Shore Hardness in Air (Shore A, 125 °C, 168 hr)
2.0
Shore Hardness (Shore A, 1.90 mm, Compression Molded)
68
Change in Durometer Hardness in Air (Shore A, 125 °C, 168 hr)
2.0
Durometer Hardness (Shore A, 1.90 mm, Compression Molded)
68
Compression Set (24 °C, 22 hr, Method B)
14 %
Compression Set (100 °C, 22 hr, Method B)
64 %
Compression Set (24 °C, 22 hr)
14 %
Compression Set (100 °C, 22 hr)
64 %
Taber Abrasion Resistance (CS-17 Wheel, 1000 g, 1000 Cycles)
5.00 mg
Processing (Melt) Temp
177 °C
UL File Number (USA)
E51193