Typical Properties
Density
1.10 g/cm³
Density - Specific Gravity
1.10 g/cm³
Change in Volume (in Reference Fuel B, 27 °C, 168 hr)
25 %
Change in Volume (in Reference Fuel B, 27 °C, 168 hr)
25 %
Change in Volume (in ASTM #1 Oil, 100 °C, 168 hr)
-19 %
Change in Volume (in ASTM #1 Oil, 100 °C, 168 hr)
-19 %
Change in Volume (in IRM 903 Oil, 100 °C, 168 hr)
16 %
Change in Volume (in IRM 903 Oil, 100 °C, 168 hr)
16 %
Change in Volume (in Water, 100 °C, 168 hr)
8.0 %
Change in Volume (in Water, 100 °C, 168 hr)
8.0 %
Melt Viscosity (190 °C, 300 sec^-1)
365 Pa·s
Tensile Stress at 100% (1.90 mm)
2.90 MPa
Tensile Stress at 100% (1.90 mm)
2.90 MPa
Tensile Stress at 100% (125 °C, 1.90 mm)
2.70 MPa
Tensile Stress at 100% (125 °C, 1.90 mm)
2.70 MPa
Tensile Stress at Yield (1.90 mm)
8.00 MPa
Tensile Stress at Yield (125 °C, 1.90 mm)
7.60 MPa
Tensile Strength at Yield (1.90 mm)
8.00 MPa
Tensile Strength at Yield (125 °C, 1.90 mm)
7.60 MPa
Tensile Strain at Break (1.90 mm)
410 %
Tensile Strain at Break (125 °C, 1.90 mm)
390 %
Torsion Modulus (24 °C, 1.9 mm)
2.2 MPa
Torsion Modulus (-20 °C, 1.9 mm)
5.9 MPa
Tensile Set
9 %
Clash-Berg Modulus (-40 °C)
68.9 MPa
Tensile Elongation at Break (125 °C, 1.90 mm)
390 %
Tensile Elongation at Break (1.90 mm)
410 %
Tear Strength (Die C, 1.90 mm)
27.1 kN/m
Ductile/Brittle Transition Temperature
-87 °C
Ductile/Brittle Transition Temperature
-87 °C
Change in Shore Hardness in Air (Shore A, 125 °C, 168 hr)
4.0
Shore Hardness (Shore A, 1.90 mm, Compression Molded)
59
Change in Durometer Hardness in Air (Shore A, 125 °C, 168 hr)
4.0
Durometer Hardness (Shore A, 1.90 mm, Compression Molded)
59
Compression Set (24 °C, 22 hr, Method B)
13 %
Compression Set (100 °C, 22 hr, Method B)
62 %
Compression Set (24 °C, 22 hr)
13 %
Compression Set (100 °C, 22 hr)
62 %
Taber Abrasion Resistance (CS-17 Wheel, 1000 g, 1000 Cycles)
5.00 mg
Processing (Melt) Temp
177 °C
UL File Number (USA)
E51193