Description
Centrex ASA 485CS NAT 000000NAT is a Acrylonitrile Styrene Acrylate material and is typically used in Coextrusion, Extrusion, Thermoforming applications. Features include: Good Melt Strength, Good Weather Resistance, Low Gloss, Medium Impact Resistance, and UV Resistant.
Availability
North America
Typical Properties
Melt Flow Rate (220 °C/10.0 kg)
5.0 g/10 min
Melt Flow Rate (220 °C/10.0 kg)
6.1 g/10 min
Density (23 °C, Method A)
1.07 g/cm³
Density - Specific Gravity
1.06 g/cm³
Tensile Modulus (5.1 mm/min)
1450 MPa
Tensile Strength at Yield (5.1 mm/min)
26.5 MPa
Flexural Modulus (1.3 mm/min, Tangent)
1380 MPa
Flexural Strength (1.3 mm/min)
38.6 MPa
Instrumented Dart Impact (23 °C, Total Energy)
24.0 J
Instrumented Dart Impact (-30 °C, Total Energy)
6.00 J
Instrumented Dart Impact (-18 °C, Total Energy)
16.0 J
Notched Izod Impact (-40 °C, 3.18 mm)
43 J/m
Notched Izod Impact (23 °C, 3.18 mm)
130 J/m
Notched Izod Impact (-18 °C, 3.18 mm)
64 J/m
Rockwell Hardness (R-Scale)
69
Vicat Softening Temperature
100 °C
Deflection Temperature Under Load Unannealed (264 psi) (3.18 mm)
68.3 °C
Coefficent of Linear Thermal Expansion (CLTE), Flow
9.4E-05 cm/cm/°C
Gloss (60°)
20
Gloss (60°)
10
Drying Temperature
82 to 93 °C
Drying Time
3.0 to 4.0 hr
Melt Temperature
204 to 243 °C
Suggested Max Moisture
<0.030 %
Die Temperature
210 to 241 °C
Suggested Max Regrind
40 %
Flame Rating (1.5 mm)
HB
UL File Number (USA)
E150937