Typical Properties
Melt Flow Rate (190 °C/2.16 kg)
3.0 g/10 min
Density (23 °C)
0.960 g/cm³
Tensile Strength at Break MD
psi
Tensile Strength at Break MD
MPa
Tensile Strength at Break TD
psi
Tensile Strength at Break TD
MPa
Tensile Strength at Yield MD
3200 psi
Tensile Strength at Yield MD
22.1 MPa
Tensile Strength at Yield TD
4060 psi
Tensile Strength at Yield TD
28.0 MPa
Tensile Elongation at Break MD
790 %
Tensile Elongation at Break TD
720 %
Secant Modulus MD
772 MPa
Secant Modulus MD
112000 psi
Secant Modulus TD
917 MPa
Secant Modulus TD
133000 psi
Elmendorf Tear Strength MD
90 g
Elmendorf Tear Strength TD
90 g