FPP3B30HB BLK
Description
FPP3B30HBBK is a 30% Glass-Reinforced, Heat-Stabilized Polypropylene
Availability
North America
Product data and technical information
Typical Properties
Melt Flow Rate
8.7 g/10 min
Density - Specific Gravity
1.14 g/cm³
Tensile Strength at Yield (23 °C)
64.1 MPa
Flexural Modulus (Tangent)
4700 MPa
Tensile Elongation at Yield
11 %
Gardner Impact
1.69 J
Notched Izod Impact (23 °C, 3.18 mm)
160 J/m
Deflection Temperature Under Load Unannealed (264 psi)
143 °C
Deflection Temperature Under Load Unannealed (66 psi)
157 °C
Drying Temperature
82 to 104 °C
Drying Time
2.0 to 4.0 hr
Rear Temperature
199 to 243 °C
Middle Temperature
199 to 243 °C
Front Temperature
199 to 243 °C
Processing (Melt) Temp
199 to 243 °C
Mold Temperature
16 to 66 °C
Screw Speed
20 to 60 rpm
Back Pressure
<0.345 MPa
Injection Rate
Moderate
Cushion
6.35 to 12.7 mm
Flame Rating (UL 94)
HB