Hifax CA 212 A



Hifax CA 212 A is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell’ s proprietary Catalloy process technology.
It has been developed for industrial applications where a combination of good processability and excellent softness is required.
The grade is available in natural pellet form.


Asia-Pacific, Australia and New Zealand, Europe, North America, South & Central America


SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin

Product Data and Technical Information

Typical Properties

Melt Flow Rate (230 °C/2.16 kg) 8 g/10 min
Density (23 °C, Method A) 0.88 g/cm³
Flexural Modulus 80 MPa
Tensile Stress at Break 10 MPa
Tensile Stress at Yield 6 MPa
Tensile Elongation at Break >600 %
Tensile Strain at Yield >40 %
Charpy Impact Strength - Notched (23 °C) NB kJ/m²
Charpy Impact Strength - Notched (-20 °C) 105 kJ/m²
Charpy Impact Strength - Notched (-40 °C) 4 kJ/m²
Shore Hardness (Shore D) 30
Vicat Softening Temperature (A50) 56 °C
Deflection Temperature Under Load (0.45 MPa, Unannealed) 40 °C
Melting Temperature 142 °C

Technical Data Sheet

Technical Data Sheet


Calendaring, Compounding, Extrusion Coating, Injection Molding, Sheet




Automotive Flooring, Polymer Modifier, Single Ply Roofing, TPO Foils and Skins

Prohibited Applications of Compounded Polyolefins:

The following applications and/or end uses are prohibited by LyondellBasell.  LyondellBasell will not solicit the sale of, or knowingly supply, product for use in the following applications:

FDA Class III medical devices, European Class III medical devices, Health Canada Class IV Medical Devices, applications involving permanent implantation into the body & life-sustaining medical applications