Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
7 g/10 min
Melt Volume Flow Rate (230 °C/2.16 kg)
8 cm³/10 min
Density (23 °C)
1.12 g/cm³
Flexural Modulus (23 °C, Tech. A)
6800 MPa
Flexural Strength (23 °C, Tech. A)
145 MPa
Tensile Modulus (23 °C)
6500 MPa
Tensile Stress at Break (23 °C)
100 MPa
Tensile Strain at Break (23 °C)
3 %
Charpy Impact Strength - Notched (23 °C)
11 kJ/m²
Charpy Impact Strength - Notched (-30 °C)
9 kJ/m²
Charpy Impact Strength - Unnotched (23 °C)
56 kJ/m²
Vicat Softening Temperature (B50)
130 °C
Deflection Temperature Under Load (1.80 MPa, Unannealed)
140 °C