Hostacom G2 N02
Description
Hostacom G2 N02 is a 20% glass fiber reinforced PP homopolymer with low melt flow rate.
Availability
Europe, North America
Product data and technical information
Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
1.0 g/10 min
Melt Volume Flow Rate (230 °C/5.0 kg)
5.5 cm³/10 min
Density (23 °C)
1.05 g/cm³
Density (23 °C)
1.05 g/cm³
Flexural Modulus (23 °C)
4400 MPa
Flexural Modulus (23 °C, Tech. A)
4000 MPa
Tensile Modulus (23 °C)
4500 MPa
Tensile Stress at Yield (23 °C)
65 MPa
Tensile Stress at Yield (23 °C, 50 mm/min)
70 MPa
Tensile Strain at Yield (23 °C)
4 %
Charpy Impact Strength - Notched (23 °C)
10 kJ/m²
Charpy Impact Strength - Notched (23 °C)
10 kJ/m²
Charpy Impact Strength - Unnotched (23 °C)
40 kJ/m²
Vicat Softening Temperature (B50)
125 °C
Deflection Temperature Under Load (0.45 MPa, Unannealed)
130 °C
Mold Shrinkage
Prohibited Applications of Compounded Polyolefins:
The following applications and/or end uses are prohibited by LyondellBasell. LyondellBasell will not solicit the sale of, or knowingly supply, product for use in the following applications:
FDA Class III medical devices, European Class III medical devices, Health Canada Class IV Medical Devices, applications involving permanent implantation into the body & life-sustaining medical applications