Hostacom M2 R19 L

Description

Hostacom M2 R19 L is a mineral filled PP copolymer with low melt flow rate.
Product is UL listed.

Availability

Europe

Product data and technical information
Typical Properties
Melt Flow Rate (230 °C/2.16 kg) 5 g/10 min
Melt Volume Flow Rate (230 °C/2.16 kg) 5 cm³/10 min
Density (23 °C) 1.07 g/cm³
Flexural Modulus (23 °C, Tech. A) 2500 MPa
Tensile Modulus (23 °C) 2500 MPa
Tensile Stress at Yield (23 °C) 27 MPa
Tensile Strain at Yield (23 °C) 4 %
Charpy Impact Strength - Notched (23 °C) 5 kJ/m²
Charpy Impact Strength - Notched (0 °C) 2.5 kJ/m²
Charpy Impact Strength - Unnotched (23 °C) 65 kJ/m²
Charpy Impact Strength - Unnotched (0 °C) 30 kJ/m²
Vicat Softening Temperature (B50) 70 °C
Deflection Temperature Under Load (0.45 MPa, Unannealed) 115 °C
Deflection Temperature Under Load (1.80 MPa, Unannealed) 62 °C
Product Stewardship Bulletin Product Stewardship Bulletin - Americas
Product Stewardship Bulletin - Europe
Product Stewardship Bulletin - Australia and New Zealand
Product Stewardship Bulletin - Africa - Middle East
Product Stewardship Bulletin - Asia - Pacific
Technical Data Sheet Technical Data Sheet
Safety Data Sheet Safety Data Sheet- Global
Marketing Polypropylene
Prohibited Applications of Compounded Polyolefins:

The following applications and/or end uses are prohibited by LyondellBasell.  LyondellBasell will not solicit the sale of, or knowingly supply, product for use in the following applications:

FDA Class III medical devices, European Class III medical devices, Health Canada Class IV Medical Devices, applications involving permanent implantation into the body & life-sustaining medical applications