Moplen HP400H
Description
Moplen HP400H is a homopolymer for extrusion and compounding applications.
Moplen HP400H exhibits easy processability and a good stiffness/impact balance at ambient temperature.
It is typically used by customers in applications such as: thermoformed tubs, containers, medium draw trays and blister packs, flowerpots and small extrusion blow moulded bottles.
Availability
Africa-Middle East, Europe
Product data and technical information
Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
2 g/10 min
Melt Flow Rate (230 °C/2.16 kg)
2.1 g/10 min
Density
0.90 g/cm³
Density (23 °C)
0.90 g/cm³
Flexural Modulus
1450 MPa
Tensile Modulus
1450 MPa
Tensile Strength at Yield
33 MPa
Tensile Stress at Yield
34 MPa
Tensile Elongation at Break (23 °C)
11 %
Tensile Strain at Break
>50 %
Tensile Strain at Yield
11 %
Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A)
8 kJ/m²
Notched Izod Impact Strength (23 °C)
40 J/m
Vicat Softening Temperature (A/50)
150 °C
Deflection Temperature Under Load (0.46 N/mm²)
95 °C
Heat Deflection Temperature B (0.45 MPa, Unannealed)
80 °C