Description
Moplen RP225M is a controlled rheology medium modified propylene random copolymer for manufacturing of high transparent cast films. The product contains slip and anti-block agents.
Moplen RP225M offers very good processability, excellent clarity and gloss and exhibits very good heat weldability.
Availability
Africa-Middle East, Europe
Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
8.0 g/10 min
Density
0.90 g/cm³
Flexural Modulus
700 N/mm²
Tensile Stress at Break (23 °C, 50 mm/min)
26.0 N/mm²
Tensile Stress at Yield (23 °C, 50 mm/min)
23.0 N/mm²
Tensile Strain at Break (23 °C, 50 mm/min)
600 %
Tensile Strain at Yield (23 °C, 50 mm/min)
14.0 %
Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A)
10.0 kJ/m²
Charpy Impact Strength - Notched (0 °C, Type 1, Edgewise, Notch A)
3.0 kJ/m²
Vicat Softening Temperature (A50)
125 °C
Deflection Temperature Under Load (0.46 N/mm²)
60 °C
Slip Erucamide
2000 ppm
Antiblock
1500 ppm