Typical Properties
Melt Volume Flow Rate (230 °C/2.16 kg)
19 cm³/10 min
Density (Method A)
1.35 g/cm³
Tensile Modulus (1 mm/min, Type 1A)
3000 MPa
Tensile Stress at Yield (Type 1A, 50 mm/min)
21.0 MPa
Tensile Strain at Yield (Type 1A, 50 mm/min)
2.5 %
Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A)
2.5 kJ/m²
Charpy Impact Strength - Notched (-30 °C, Type 1, Edgewise, Notch A)
2.3 kJ/m²
Charpy Impact Strength - Unnotched (23 °C, Type 1, Edgewise)
20 kJ/m²
Charpy Impact Strength - Unnotched (-30 °C, Type 1, Edgewise)
8.5 kJ/m²
Ball Pressure Test (125 °C)
Pass
Vicat Softening Temperature (A (10N), 50 °C/h)
145 °C
Vicat Softening Temperature (B (50N), 50 °C/h)
82.0 °C
Deflection Temperature Under Load Unannealed (0.45 MPa) (Flatwise)
118 °C
Deflection Temperature Under Load Unannealed (1.80 MPa) (Flatwise)
60.0 °C
RTI Elec (1.5 mm)
105 °C
RTI Elec (3.0 mm)
105 °C
RTI Imp (1.5 mm)
105 °C
RTI Imp (3.0 mm)
105 °C
RTI Str (1.5 mm)
105 °C
RTI Str (3.0 mm)
105 °C
Surface Resistivity
>1.0E+15 ohm
Volume Resistivity
>1.0E+13 ohm*m
Comparative Tracking Index (CTI)
600 V
Burning Rate (2.00 mm, Self-Extinguishing)
0.0 mm/min
Burning Rate (2.00 mm, Self-Extinguishing)
0.0 mm/min
Glow Wire Flammability Index (1.5 mm)
960 °C
Glow Wire Flammability Index (3.0 mm)
960 °C
Glow Wire Ignition Temperature (1.5 mm)
700 °C
Glow Wire Ignition Temperature (3.0 mm)
700 °C
Oxygen Index
26 %
Water Absorption 23C/50RH
0.16 %
Drying Temperature
70 to 80 °C
Drying Time
2.0 to 4.0 hr
Rear Temperature
180 °C
Middle Temperature
200 °C
Front Temperature
210 °C
Nozzle Temperature
220 °C
Processing (Melt) Temp
180 to 220 °C
Mold Temperature
40 to 80 °C
Screw Speed
<300 mm/sec
Holding Pressure
40.0 to 90.0 MPa
Back Pressure
5.00 to 10.0 MPa
Injection Pressure
80.0 to 120 MPa
Injection Rate
Slow-Moderate
Cushion
<5.00 mm
Flame Rating (1.5 mm)
V-0
Flame Rating (3.0 mm)
V-0
Flammability Classification (1.5 mm)
V-0
Flammability Classification (3.0 mm)
V-0
UL File Number
E86615