Typical Properties
Melt Volume Flow Rate (230 °C/2.16 kg)
5.0 cm³/10 min
Density (Method A)
1.13 g/cm³
Tensile Modulus (1 mm/min, Type 1A)
6500 MPa
Tensile Strain at Break (Type 1A, 5 mm/min)
2.8 %
Flexural Modulus (2.0 mm/min)
6000 MPa
Flexural Stress (2.0 mm/min, 3.6%)
126 MPa
Flexural Stress (2.0 mm/min, 3.4%)
128 MPa
Tensile Stress at Break (Type 1A, 5 mm/min)
84.0 MPa
Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A)
10 kJ/m²
Charpy Impact Strength - Notched (-30 °C, Type 1, Edgewise, Notch A)
8.0 kJ/m²
Charpy Impact Strength - Unnotched (23 °C, Type 1, Edgewise)
48 kJ/m²
Charpy Impact Strength - Unnotched (-30 °C, Type 1, Edgewise)
45 kJ/m²
Ball Indentation Hardness (H 358/30)
120 MPa
Ball Pressure Test (145 °C)
Pass
Vicat Softening Temperature (A (10N), 50 °C/h)
165 °C
Vicat Softening Temperature (B (50N), 50 °C/h)
130 °C
Deflection Temperature Under Load Unannealed (0.45 MPa) (Flatwise)
159 °C
Deflection Temperature Under Load Unannealed (1.80 MPa) (Flatwise)
160 °C
Surface Resistivity
>1.0E+15 ohm
Volume Resistivity
>1.0E+13 ohm*m
Burning Rate (2.00 mm)
58 mm/min
Burning Rate (2.00 mm)
58 mm/min
Glow Wire Flammability Index (1.5 mm)
775 °C
Glow Wire Flammability Index (3.0 mm)
775 °C
Glow Wire Ignition Temperature (1.5 mm)
800 °C
Glow Wire Ignition Temperature (3.0 mm)
800 °C
Drying Temperature
80 °C
Drying Time
2.0 to 3.0 hr
Processing (Melt) Temp
220 to 260 °C
Mold Temperature
30 to 60 °C
Injection Rate
Moderate-Fast
Flammability Classification (1.5 mm)
HB
Flammability Classification (3.0 mm)
HB
UL File Number
E86615