Typical Properties
Melt Volume Flow Rate (220 °C/10.0 kg)
25 cm³/10 min
Density (Method A)
1.06 g/cm³
Tensile Modulus (1 mm/min, Type 1A)
2600 MPa
Tensile Stress at Yield (Type 1A, 50 mm/min)
50.0 MPa
Tensile Strain at Yield (Type 1A, 50 mm/min)
3.0 %
Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A)
15 kJ/m²
Charpy Impact Strength - Notched (-30 °C, Type 1, Edgewise, Notch A)
7.0 kJ/m²
Charpy Impact Strength - Unnotched (23 °C, Type 1, Edgewise)
91 kJ/m²
Charpy Impact Strength - Unnotched (-30 °C, Type 1, Edgewise)
58 kJ/m²
Ball Indentation Hardness (H 358/30)
120 MPa
Vicat Softening Temperature (A (10N), 50 °C/h)
103 °C
Vicat Softening Temperature (B (50N), 50 °C/h)
97.0 °C
Deflection Temperature Under Load Unannealed (0.45 MPa) (Flatwise)
88.0 °C
Deflection Temperature Under Load Unannealed (1.80 MPa) (Flatwise)
77.0 °C
Burning Rate (2.00 mm)
<100 mm/min
Burning Rate (2.00 mm)
<100 mm/min
Glow Wire Flammability Index (1.5 mm)
675 °C
Glow Wire Flammability Index (3.0 mm)
675 °C
Glow Wire Ignition Temperature (1.5 mm)
700 °C
Glow Wire Ignition Temperature (3.0 mm)
700 °C
Flammability Classification (1.5 mm)
HB
Flammability Classification (3.0 mm)
HB
UL File Number
E86615