Typical Properties
Melt Volume Flow Rate (230 °C/3.8 kg)
10 cm³/10 min
Density (Method A)
1.08 g/cm³
Tensile Modulus (1 mm/min, Type 1A)
3700 MPa
Tensile Stress at Break (Type 1A, 5 mm/min)
70.0 MPa
Tensile Strain at Break (Type 1A, 5 mm/min)
3.0 %
Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A)
3.0 kJ/m²
Charpy Impact Strength - Unnotched (23 °C, Type 1, Edgewise)
17 kJ/m²
Ball Indentation Hardness (H 358/30)
171 MPa
Vicat Softening Temperature (A (10N), 50 °C/h)
106 °C
Vicat Softening Temperature (B (50N), 50 °C/h)
102 °C
Deflection Temperature Under Load Unannealed (0.45 MPa) (Flatwise)
103 °C
Deflection Temperature Under Load Unannealed (1.80 MPa) (Flatwise)
100 °C
Rear Temperature
180 to 200 °C
Middle Temperature
210 to 230 °C
Front Temperature
240 to 250 °C
Nozzle Temperature
240 to 260 °C
Processing (Melt) Temp
220 to 250 °C
Mold Temperature
50 to 80 °C
Screw Speed
<600 mm/sec
Holding Pressure
30.0 to 90.0 MPa
Back Pressure
5.00 to 15.0 MPa
Injection Pressure
100 to 150 MPa
Injection Rate
Moderate-Fast