PP5A0NANAT
Description
PP5A0 is an Unfilled, High Impact Polypropylene Copolymer
Availability
North America
Product data and technical information
Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
8.0 g/10 min
Density - Specific Gravity
0.908 g/cm³
Tensile Strength at Yield (23 °C)
20.9 MPa
Flexural Modulus (Tangent)
979 MPa
Tensile Elongation at Yield
12 %
Gardner Impact
25.3 J
Notched Izod Impact (23 °C, 3.18 mm)
640 J/m
Drying Temperature
82 to 104 °C
Drying Time
2.0 to 4.0 hr
Rear Temperature
177 to 232 °C
Middle Temperature
177 to 232 °C
Front Temperature
177 to 232 °C
Processing (Melt) Temp
193 to 232 °C
Mold Temperature
21 to 49 °C
Back Pressure
0.138 to 2.07 MPa
Injection Rate
Moderate
Cushion
6.35 to 12.7 mm