Typical Properties
Melt Flow Rate (190 °C/21.6 kg)
11.5 g/10 min
Density (23 °C)
0.949 g/cm³
Flexural Modulus (1% Secant)
1160 MPa
Flexural Modulus (1% Secant)
168000 psi
Tensile Strength at Break
33.8 MPa
Tensile Strength at Break
4900 psi
Tensile Strength at Yield
25.2 MPa
Tensile Strength at Yield
3650 psi
Tensile Elongation at Yield
1300 %
Tensile Impact Strength
249 ft-lb/in²
Tensile Impact Strength
523 kJ/m²
Shore Hardness (Shore D)
68
Vicat Softening Temperature
126 °C
Vicat Softening Temperature
259 °F
Low Temperature Brittleness F₅₀
<-105 °F
Low Temperature Brittleness F₅₀
<-76 °C
Deflection Temperature Under Load (66 psi, Unannealed)
63 °C
Deflection Temperature Under Load (66 psi, Unannealed)
145 °F