Pro-fax 6301 polypropylene homopolymer is available in spherical particle form. This resin is typically used for mixing with pigments and other additives to make polymer concentrates or masterbatches.
Pro-fax 6301 has very minimal stabilization, which allows wide design latitude for compounders. Additional stabilization is required to protect the resin during melt processing and throughout its useful life.
Please note that any additives compounded into this resin will require a re-assessment of its FDA status.
Pro-fax 6301
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (230 °C/2.16 kg) | 12 g/10 min |
| Density (23 °C) | 0.90 g/cm³ |
| Flexural Modulus (0.05 in/min, 1% Secant, Procedure A) | 210000 psi |
| Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A) | 1450 MPa |
| Tensile Strength at Yield (2 in/min) | 4900 psi |
| Tensile Strength at Yield (50 mm/min) | 34 MPa |
| Tensile Elongation at Yield | 11 % |
| Notched Izod Impact Strength (73 °F, Method A) | 0.6 ft-lb/in |
| Notched Izod Impact Strength (23 °C, Method A) | 32 J/m |
| Deflection Temperature Under Load (66 psi, Unannealed) | 200 °F |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 93 °C |
Technical Data Sheet
Technical Data Sheet - ASTMProcess
Compounding
Resin
Polypropylene, Homopolymer
Applications
Colour Concentrates, Polymer Modifier, Wood Composites