Pro-fax 6323 general purpose polypropylene homopolymer is available in pellet form. This resin is typically used in injection molding applications.
ASTM and ISO-based versions of the technical data sheet are available for Pro-fax 6323.
Pro-fax 6323
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (230 °C/2.16 kg) | 12 g/10 min |
| Density (23 °C) | 0.90 g/cm³ |
| Density (23 °C, Method A) | 0.90 g/cm³ |
| Flexural Modulus (23 °C) | 1290 MPa |
| Flexural Modulus (0.05 in/min, 1% Secant, Procedure A) | 210000 psi |
| Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A) | 1450 MPa |
| Tensile Strength at Yield (2 in/min) | 4900 psi |
| Tensile Strength at Yield (50 mm/min) | 34 MPa |
| Tensile Stress at Yield (23 °C) | 31 MPa |
| Tensile Elongation at Yield | 11 % |
| Tensile Strain at Yield (23 °C) | 11 % |
| Charpy Impact Strength - Notched (23 °C) | 4.2 kJ/m² |
| Notched Izod Impact Strength (23 °C) | 4.1 kJ/m² |
| Notched Izod Impact Strength (73 °F, Method A) | 0.6 ft-lb/in |
| Notched Izod Impact Strength (23 °C, Method A) | 32 J/m |
| Deflection Temperature Under Load (66 psi, Unannealed) | 200 °F |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 76 °C |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 93 °C |
| Deflection Temperature Under Load (1.80 MPa, Unannealed) | 49 °C |
Process
Cast Film, Injection Molding
Resin
Polypropylene, Homopolymer
Applications
Automotive Parts, Caps & Closures, Containers, Food Packaging Film, Sports, Leisure & Toys