Description
Pro-fax EP611H high impact polypropylene copolymer is available in pellet form. This resin is typically used in extrusion applications, including corrugated board, and offers very good stiffness/low temperature impact balance.
Availability
North America
Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
1.8 g/10 min
Density (23 °C)
0.90 g/cm³
Tensile Strength at Yield (2 in/min)
4100 psi
Tensile Strength at Yield (50 mm/min)
28 MPa
Flexural Modulus (0.05 in/min, 1% Secant, Procedure A)
205000 psi
Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A)
1410 MPa
Tensile Elongation at Yield
8 %
Notched Izod Impact Strength (73 °F, Method A)
2.8 ft-lb/in
Notched Izod Impact Strength (23 °C, Method A)
150 J/m
Deflection Temperature Under Load (66 psi, Unannealed)
187 °F
Deflection Temperature Under Load (0.45 MPa, Unannealed)
86 °C