Description
Pro-fax EP713H nucleated high impact polypropylene copolymer is available in pellet form. This resin is typically used in extrusion applications such as thermoforming, blow molding, and sheet extrusion.
Availability
North America
Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
1.8 g/10 min
Density (23 °C)
0.90 g/cm³
Tensile Strength at Yield (2 in/min)
4300 psi
Tensile Strength at Yield (50 mm/min)
30 MPa
Flexural Modulus (0.05 in/min, 1% Secant, Procedure A)
220000 psi
Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A)
1520 MPa
Tensile Elongation at Yield
7 %
Notched Izod Impact Strength (73 °F, Method A)
4.0 ft-lb/in
Notched Izod Impact Strength (23 °C, Method A)
214 J/m
Deflection Temperature Under Load (66 psi, Unannealed)
223 °F
Deflection Temperature Under Load (0.45 MPa, Unannealed)
106 °C