Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
35 g/10 min
Density (23 °C)
0.90 g/cm³
Density (23 °C, Method A)
0.90 g/cm³
Flexural Modulus (23 °C)
1120 MPa
Flexural Modulus (0.05 in/min, 1% Secant, Procedure A)
160000 psi
Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A)
1100 MPa
Tensile Strength at Yield (2 in/min)
3100 psi
Tensile Strength at Yield (50 mm/min)
21 MPa
Tensile Stress at Yield (23 °C)
21 MPa
Tensile Elongation at Yield
5 %
Tensile Strain at Yield (23 °C)
5 %
Charpy Impact Strength - Notched (23 °C)
11 kJ/m²
Charpy Impact Strength - Notched (-30 °C)
4.5 kJ/m²
Notched Izod Impact Strength (23 °C)
12 kJ/m²
Notched Izod Impact Strength (-40 °C)
5.3 kJ/m²
Notched Izod Impact Strength (73 °F, Method A)
2.3 ft-lb/in
Notched Izod Impact Strength (23 °C, Method A)
123 J/m
Deflection Temperature Under Load (66 psi, Unannealed)
219 °F
Deflection Temperature Under Load (0.45 MPa, Unannealed)
104 °C
Deflection Temperature Under Load (0.45 MPa, Unannealed)
83 °C
Deflection Temperature Under Load (1.80 MPa, Unannealed)
50 °C
Mold Shrinkage