Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
11 g/10 min
Density (23 °C)
0.90 g/cm³
Flexural Modulus (0.05 in/min, 1% Secant, Procedure A)
150000 psi
Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A)
1030 MPa
Tensile Strength at Yield (2 in/min)
4300 psi
Tensile Strength at Yield (50 mm/min)
30 MPa
Tensile Elongation at Yield
12 %
Notched Izod Impact Strength (73 °F, Method A)
1.2 ft-lb/in
Notched Izod Impact Strength (23 °C, Method A)
64 J/m
Deflection Temperature Under Load (66 psi, Unannealed)
170 °F
Deflection Temperature Under Load (0.45 MPa, Unannealed)
77 °C
Haze (45 mil)
7 %