Pro-fax SV152

LyondellBasell

Description

Pro-fax SV152 is a nucleated, very high impact polypropylene copolymer available in pellet form.  This resin is typically used in general extrusion and blow molding applications and offers excellent cold temperature impact resistance.

ASTM and ISO-based versions of the technical data sheet are available for Pro-fax SV152.

Availability

North America

Legend

SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin

Product Data and Technical Information

Typical Properties

Melt Flow Rate (230 °C/2.16 kg) 1.4 g/10 min
Density (23 °C) 0.90 g/cm³
Density (23 °C, Method A) 0.90 g/cm³
Flexural Modulus (23 °C) 1180 MPa
Flexural Modulus (0.05 in/min, 1% Secant, Procedure A) 165000 psi
Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A) 1140 MPa
Tensile Strength at Yield (2 in/min) 3500 psi
Tensile Strength at Yield (50 mm/min) 24 MPa
Tensile Stress at Yield (23 °C) 24 MPa
Tensile Elongation at Yield 9 %
Tensile Strain at Yield (23 °C) 8 %
Charpy Impact Strength - Notched (23 °C) 85 kJ/m²
Charpy Impact Strength - Notched (-40 °C) 4.2 kJ/m²
Notched Izod Impact Strength (23 °C) 64 kJ/m²
Notched Izod Impact Strength (-40 °C) 4.7 kJ/m²
Notched Izod Impact Strength (73 °F, Method A) No Break ft-lb/in
Notched Izod Impact Strength (23 °C, Method A) No Break J/m
Rockwell Hardness (R-Scale) 76
Rockwell Hardness (R-Scale) 76
Deflection Temperature Under Load (66 psi, Unannealed) 195 °F
Deflection Temperature Under Load (0.45 MPa, Unannealed) 78 °C
Deflection Temperature Under Load (0.45 MPa, Unannealed) 91 °C
Deflection Temperature Under Load (1.80 MPa, Unannealed) 49 °C

Process

Extrusion Blow Molding, Sheet, Sheet and Profile Extrusion, Thermoforming


Resin

Polypropylene, Impact Copolymer


Applications

Automotive Parts, Corrugated Sheet, Opaque Containers