Diamaloy QR-1220 IM Dark Grey LDR 1/100 is a Polycarbonate + ABS material. Features include: High Heat Resistance, High Impact Resistance, Impact Modified, and Low Temperature Impact Resistance.
QR-1220 IM Dark Grey LDR 1/100
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (260 °C/5.0 kg) | 20 g/10 min |
| Melt Volume Flow Rate (260 °C/5.0 kg) | 22 cm³/10 min |
| Density - Specific Gravity | 1.14 g/cm³ |
| Tensile Modulus (23 °C, 1 mm/min) | 2340 MPa |
| Tensile Stress at Yield (23 °C, 5 mm/min) | 54.5 MPa |
| Tensile Strength at Yield (23 °C) | 52.0 MPa |
| Tensile Stress at Break (23 °C, 5 mm/min) | 52.0 MPa |
| Tensile Strain at Yield (23 °C) | 3.4 % |
| Tensile Strain at Break (23 °C, 5 mm/min) | 100 % |
| Flexural Modulus (23 °C) | 2250 MPa |
| Flexural Modulus (23 °C, 2.0 mm/min, Chord, 64.0 mm) | 2560 MPa |
| Flexural Stress (23 °C, 2.0 mm/min) | 90.0 MPa |
| Flexural Strength at Yield (23 °C) | 84.8 MPa |
| Tensile Elongation at Yield (23 °C) | 150 % |
| Charpy Impact Strength - Notched (23 °C) | 46 kJ/m² |
| Charpy Impact Strength - Notched (-30 °C) | 33 kJ/m² |
| Notched Izod Impact Strength (23 °C) | 47 kJ/m² |
| Notched Izod Impact Strength (-30 °C) | 37 kJ/m² |
| Notched Izod Impact (23 °C) | 530 J/m |
| Notched Izod Impact (-30 °C) | 430 J/m |
| Vicat Softening Temperature (B (50N), 50 °C/h) | 122 °C |
| Deflection Temperature Under Load Unannealed (0.45 MPa) | 122 °C |
| Deflection Temperature Under Load Unannealed (1.80 MPa) | 104 °C |
| Deflection Temperature Under Load Unannealed (264 psi) | 104 °C |
| Coefficent of Linear Thermal Expansion (CLTE), Flow (-30 to 80 °C) | 7.5E-5 cm/cm/°C |
| Coefficent of Linear Thermal Expansion (CLTE), Perpendicular (-30 to 80 °C) | 7.6E-5 cm/cm/°C |
| Drying Time | 2.0 to 4.0 hr |
| Drying Temperature | 74 °C |
| Nozzle Temperature | 243 to 271 °C |
| Processing (Melt) Temp | 249 to 260 °C |
| Front Temperature | 243 to 271 °C |
| Middle Temperature | 243 to 271 °C |
| Rear Temperature | 227 to 254 °C |
| Mold Temperature | 38 to 71 °C |
| Drying Time, Maximum | 4 hr |