Typical Properties
Density (Method A)
1.28 g/cm³
Tensile Modulus (1 mm/min, Type 1A)
3700 MPa
Tensile Modulus (1 mm/min, Type 1A) - Conditioned
1500 MPa
Tensile Stress at Yield (Type 1A, 50 mm/min)
50.0 MPa
Tensile Stress at Yield (Type 1A, 50 mm/min) - Conditioned
33.0 MPa
Tensile Strain at Yield (Type 1A, 50 mm/min)
3.5 %
Tensile Strain at Yield (Type 1A, 50 mm/min) - Conditioned
27 %
Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A)
12 kJ/m²
Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A) - Conditioned
20 kJ/m²
Charpy Impact Strength - Notched (-30 °C, Type 1, Edgewise, Notch A)
9.0 kJ/m²
Charpy Impact Strength - Unnotched (23 °C, Type 1, Edgewise)
No Break kJ/m²
Charpy Impact Strength - Unnotched (23 °C, Type 1, Edgewise) - Conditioned
No Break kJ/m²
Charpy Impact Strength - Unnotched (-30 °C, Type 1, Edgewise)
No Break kJ/m²
Vicat Softening Temperature (A (10N), 50 °C/h)
220 °C
Vicat Softening Temperature (B (50N), 50 °C/h)
175 °C
Deflection Temperature Under Load Unannealed (0.45 MPa) (Flatwise)
180 °C
Deflection Temperature Under Load Unannealed (1.80 MPa) (Flatwise)
65.0 °C
Surface Resistivity
>1.0E+15 ohm
Surface Resistivity - Conditioned
>1.0E+12 ohm
Volume Resistivity
>1.0E+13 ohm*m
Volume Resistivity - Conditioned
>1.0E+10 ohm*m
Burning Rate (2.00 mm)
<100 mm/min
Burning Rate (2.00 mm)
<100 mm/min
Water Absorption 23C/50RH
1.4 %
Drying Temperature
80 °C
Drying Time
2.0 to 4.0 hr
Suggested Max Moisture
0.040 to 0.10 %
Processing (Melt) Temp
270 to 300 °C
Mold Temperature
70 to 100 °C
Flammability Classification (1.5 mm)
HB
Flammability Classification (3.0 mm)
HB