Typical Properties
Melt Volume Flow Rate (265 °C/2.16 kg)
26 cm³/10 min
Density (Method A)
1.18 g/cm³
Tensile Modulus (1 mm/min, Type 1A)
1600 MPa
Tensile Stress at Yield (Type 1A, 50 mm/min)
47.0 MPa
Tensile Stress at Break (Type 1A, 50 mm/min)
42.0 MPa
Tensile Strain at Yield (Type 1A, 50 mm/min)
6.0 %
Nominal Tensile Strain at Break (50 mm/min, Type 1A)
130 %
Flexural Modulus (2.0 mm/min)
1800 MPa
Flexural Stress (2.0 mm/min, 3.5%)
58.0 MPa
Flexural Stress (2.0 mm/min, 9.0%)
65.0 MPa
Flexural Stress (2.0 mm/min, 6.2%)
72.0 MPa
Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A)
80 kJ/m²
Charpy Impact Strength - Notched (-30 °C, Type 1, Edgewise, Notch A)
7.0 kJ/m²
Charpy Impact Strength - Unnotched (23 °C, Type 1, Edgewise)
No Break kJ/m²
Charpy Impact Strength - Unnotched (-30 °C, Type 1, Edgewise)
No Break kJ/m²
Ball Indentation Hardness (H 358/30)
91.0 MPa
Vicat Softening Temperature (A (10N), 50 °C/h)
104 °C
Vicat Softening Temperature (B (50N), 50 °C/h)
98.0 °C
Deflection Temperature Under Load Unannealed (0.45 MPa) (Flatwise)
86.0 °C
Deflection Temperature Under Load Unannealed (1.80 MPa) (Flatwise)
80.0 °C
Surface Resistivity
>1.0E+15 ohm
Volume Resistivity
>1.0E+13 ohm*m
Burning Rate (2.00 mm)
<100 mm/min
Burning Rate (2.00 mm)
<100 mm/min
Drying Time
4 hr
Drying Temperature
90 °C
Suggested Max Moisture
5.0E-3 to 0.015 %
Processing (Melt) Temp
280 °C
Mold Temperature
60 to 80 °C
Flammability Classification (1.5 mm)
HB
Flammability Classification (3.0 mm)
HB