Typical Properties
Density (Method A)
1.57 g/cm³
Tensile Modulus (1 mm/min, Type 1A)
16500 MPa
Tensile Modulus (1 mm/min, Type 1A) - Conditioned
13000 MPa
Tensile Stress at Break (Type 1A, 5 mm/min)
228 MPa
Tensile Stress at Break (Type 1A, 5 mm/min) - Conditioned
180 MPa
Tensile Strain at Break (Type 1A, 5 mm/min)
2.3 %
Tensile Strain at Break (Type 1A, 5 mm/min) - Conditioned
3.3 %
Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A)
14 kJ/m²
Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A) - Conditioned
18 kJ/m²
Charpy Impact Strength - Notched (-30 °C, Type 1, Edgewise, Notch A)
12 kJ/m²
Charpy Impact Strength - Unnotched (23 °C, Type 1, Edgewise)
90 kJ/m²
Charpy Impact Strength - Unnotched (23 °C, Type 1, Edgewise) - Conditioned
94 kJ/m²
Charpy Impact Strength - Unnotched (-30 °C, Type 1, Edgewise)
70 kJ/m²
Ball Indentation Hardness (H 358/30)
300 MPa
Ball Indentation Hardness (H 358/30) - Conditioned
220 MPa
Vicat Softening Temperature (A (10N), 50 °C/h)
>250 °C
Vicat Softening Temperature (B (50N), 50 °C/h)
>250 °C
Deflection Temperature Under Load Unannealed (0.45 MPa) (Flatwise)
>250 °C
Deflection Temperature Under Load Unannealed (1.80 MPa) (Flatwise)
>250 °C
RTI Elec (1.5 mm)
120 °C
RTI Elec (3.0 mm)
120 °C
RTI Elec (0.75 mm)
120 °C
RTI Imp (1.5 mm)
105 °C
RTI Imp (3.0 mm)
115 °C
RTI Imp (0.75 mm)
105 °C
RTI Str (1.5 mm)
120 °C
RTI Str (3.0 mm)
130 °C
RTI Str (0.75 mm)
120 °C
Surface Resistivity
>1.0E+15 ohm
Surface Resistivity - Conditioned
>1.0E+12 ohm
Volume Resistivity
>1.0E+13 ohm*m
Volume Resistivity - Conditioned
>1.0E+10 ohm*m
Comparative Tracking Index (CTI)
450 V
Burning Rate (2.00 mm)
30 mm/min
Burning Rate (2.00 mm)
30 mm/min
Glow Wire Flammability Index (1.5 mm)
600 °C
Glow Wire Flammability Index (3.0 mm)
600 °C
Water Absorption 23C/50RH
1.2 %
Drying Temperature
80 °C
Drying Time
3.0 to 4.0 hr
Suggested Max Moisture
0.040 to 0.10 %
Processing (Melt) Temp
280 to 300 °C
Mold Temperature
60 to 120 °C
Flammability Classification (0.75 mm)
HB
Flammability Classification (1.5 mm)
HB
Flammability Classification (3.0 mm)
HB
UL File Number
E86615