SCHULATEC PP EVC 01 BLK
Description
Schulatec PP EVC 01 BLACK EXP is an experimental PP compound with special rubber modification for extruded EV battery cooling tubes.
Availability
Europe
Product data and technical information
Typical Properties
Melt Volume Flow Rate (230 °C/2.16 kg)
4.0 cm³/10 min
Melt Volume Flow Rate (230 °C/5.0 kg)
20 cm³/10 min
Density
0.91 g/cm³
Tensile Modulus (23 °C)
1000 MPa
Tensile Stress at Yield (Type 1, 23 °C, 50 mm/min)
18 MPa
Tensile Strain at Yield (Type 1A, 23 °C, 50 mm/min)
15 %
Nominal Tensile Strain at Break (23 °C)
>400 %
Flexural Modulus (23 °C)
1100 MPa
Flexural Stress (23 °C)
25 MPa
Charpy Impact Strength - Notched (23 °C)
30 kJ/m²
Charpy Impact Strength - Notched (-40 °C)
5 kJ/m²
Charpy Impact Strength - Unnotched (23 °C)
No Break kJ/m²
Charpy Impact Strength - Unnotched (-40 °C)
No Break kJ/m²
Deflection Temperature Under Load (0.45 MPa, Unannealed)
80 °C
Deflection Temperature Under Load (1.80 MPa, Unannealed)
50 °C
Burning Rate
<100 mm/min
Melt Temperature
210-230 °C