Typical Properties
Melt Flow Rate (190 °C/2.16 kg)
0.34 g/10 min
Density (23 °C)
0.944 g/cm³
Tensile Strength at Break MD
7450 psi
Tensile Strength at Break MD
51.4 MPa
Tensile Strength at Break TD
46.2 MPa
Tensile Strength at Break TD
6700 psi
Tensile Strength at Yield MD
22.1 MPa
Tensile Strength at Yield MD
3200 psi
Tensile Strength at Yield TD
27.6 MPa
Tensile Strength at Yield TD
4000 psi
Tensile Elongation at Break MD
590 %
Tensile Elongation at Break TD
850 %
Secant Modulus MD
98500 psi
Secant Modulus MD
679 MPa
Secant Modulus TD
132000 psi
Secant Modulus TD
910 MPa
Elmendorf Tear Strength MD
49 g
Elmendorf Tear Strength TD
1100 g