Typical Properties
Melt Flow Rate (190 °C/2.16 kg)
0.027 g/10 min
Density (23 °C)
0.949 g/cm³
Dart Drop Impact Strength, F50
230 g
Tensile Strength at Break MD
11600 psi
Tensile Strength at Break MD
80.0 MPa
Tensile Strength at Break TD
52.4 MPa
Tensile Strength at Break TD
7600 psi
Tensile Strength at Yield MD
5400 psi
Tensile Strength at Yield MD
37.2 MPa
Tensile Strength at Yield TD
4100 psi
Tensile Strength at Yield TD
28.3 MPa
Tensile Elongation at Break MD
330 %
Tensile Elongation at Break TD
410 %
Secant Modulus MD
993 MPa
Secant Modulus MD
144000 psi
Secant Modulus TD
1020 MPa
Secant Modulus TD
148000 psi
Elmendorf Tear Strength MD
10 g
Elmendorf Tear Strength TD
60 g