Typical Properties
Melt Flow Rate (190 °C/2.16 kg)
0.45 g/10 min
Density (23 °C)
0.950 g/cm³
Tensile Strength at Break MD
43.1 MPa
Tensile Strength at Break MD
6250 psi
Tensile Strength at Break TD
30.5 MPa
Tensile Strength at Break TD
4420 psi
Tensile Strength at Yield MD
23.4 MPa
Tensile Strength at Yield MD
3400 psi
Tensile Strength at Yield TD
23.2 MPa
Tensile Strength at Yield TD
3370 psi
Tensile Elongation at Break MD
530 %
Tensile Elongation at Break TD
970 %
Secant Modulus MD
101000 psi
Secant Modulus MD
695 MPa
Secant Modulus TD
132000 psi
Secant Modulus TD
910 MPa
Elmendorf Tear Strength MD
40 g
Elmendorf Tear Strength TD
900 g