Typical Properties
Melt Flow Rate (190 °C/2.16 kg)
0.85 g/10 min
Density (23 °C)
0.958 g/cm³
Tensile Strength at Break MD
54.5 MPa
Tensile Strength at Break MD
7900 psi
Tensile Strength at Break TD
3400 psi
Tensile Strength at Break TD
23.4 MPa
Tensile Strength at Yield MD
3700 psi
Tensile Strength at Yield MD
25.5 MPa
Tensile Strength at Yield TD
3800 psi
Tensile Strength at Yield TD
26.2 MPa
Tensile Elongation at Break MD
700 %
Tensile Elongation at Break TD
750 %
Secant Modulus MD
938 MPa
Secant Modulus MD
136000 psi
Secant Modulus TD
184000 psi
Secant Modulus TD
1270 MPa
Elmendorf Tear Strength MD
30 g
Elmendorf Tear Strength TD
900 g