Typical Properties
Melt Flow Rate (190 °C/2.16 kg)
1.15 g/10 min
Density (23 °C)
0.954 g/cm³
Tensile Strength at Break MD
41.2 MPa
Tensile Strength at Break MD
5980 psi
Tensile Strength at Break TD
6110 psi
Tensile Strength at Break TD
42.1 MPa
Tensile Strength at Yield MD
3780 psi
Tensile Strength at Yield MD
26.1 MPa
Tensile Strength at Yield TD
31.1 MPa
Tensile Strength at Yield TD
4510 psi
Tensile Elongation at Break MD
750 %
Tensile Elongation at Break TD
920 %
Secant Modulus MD
814 MPa
Secant Modulus MD
118000 psi
Secant Modulus TD
156000 psi
Secant Modulus TD
1080 MPa
Elmendorf Tear Strength MD
60 g
Elmendorf Tear Strength TD
260 g