Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
2.0 g/10 min
Density (23 °C)
0.90 g/cm³
Flexural Modulus (0.05 in/min, 1% Secant, Procedure A)
140000 psi
Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A)
965 MPa
Tensile Strength at Yield (2 in/min)
4300 psi
Tensile Strength at Yield (50 mm/min)
30 MPa
Tensile Elongation at Yield
14 %
Notched Izod Impact Strength (73 °F, Method A)
7.0 ft-lb/in
Notched Izod Impact Strength (23 °C, Method A)
370 J/m
Deflection Temperature Under Load (66 psi, Unannealed)
165 °F
Deflection Temperature Under Load (0.45 MPa, Unannealed)
74 °C
Haze (45 mil)
9 %