Typical Properties
Equivalent Melt Index
3.0 g/10 min
Density (23 °C)
0.931 g/cm³
Vinyl Acetate Content
12 %
Tensile Modulus (1% Secant)
18500 psi
Tensile Modulus (1% Secant)
127 MPa
Tensile Strength at Break
2100 psi
Tensile Strength at Break
14.5 MPa
Tensile Elongation at Break
1100 %
Shore Hardness (Shore D)
44
Vicat Softening Temperature
69 °C
Vicat Softening Temperature
156 °F
Low Temperature Brittleness
<-76 °C
Low Temperature Brittleness
<-105 °F
DSC Melting Point
93 °C
DSC Melting Point
199 °F