Adflex Z 101 H is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell’ s proprietary Catalloy process technology.
It exhibits high softness and low modulus, with high melt flow index.
Adflex Z 101 H is tailored to replace atactic polypropylene copolymers (APP) used for the modification of bitumen in roofing membranes. The percentage to be added can vary according to the quantity of the atactic polypropylene used in combination with Adflex Z 101 H and the requested cold bending temperature of the end product. Its structure is tailored to obtain easy dispersion and phase inversion in the bitumen blend.
The grade is available in natural pellet form.
Adflex Z101H
Description
Availability
Africa-Middle East, Asia-Pacific, Australia and New Zealand, Europe, North America, South & Central America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (230 °C/2.16 kg) | 27 g/10 min |
| Density (23 °C, Method A) | 0.88 g/cm³ |
| Flexural Modulus | 80 MPa |
| Tensile Stress at Break | 10 MPa |
| Tensile Stress at Yield | 5 MPa |
| Tensile Strain at Break | 800 % |
| Tensile Strain at Yield | 45 % |
| Charpy Impact Strength - Notched (23 °C) | NB kJ/m² |
| Charpy Impact Strength - Notched (-20 °C) | 100 kJ/m² |
| Charpy Impact Strength - Notched (-40 °C) | 2 kJ/m² |
| Shore Hardness (Shore D) | 30 |
| Vicat Softening Temperature (A50) | 53 °C |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 38 °C |
| Melting Temperature | 142 °C |
Technical Data Sheet
Technical Data SheetProcess
Compounding, Continuous Filament/Spinning, Extrusion Coating, Extrusion Flat-die, Fibers, Injection Molding, Spunbond, Staple Fiber
Resin
Catalloy
Applications
Bitumen Modification, Bulk Continuous Filament & Continuous Filament, Carpet Backing, Filament Yarn, Hygiene Nonwoven, Impact Modification, Nonwovens, Soft Touch Applications