Description
Adstif HA801U very high melt flow, nucleated polypropylene homopolymer is available in pellet form. This resin is typically used in high-speed injection molding of thin-walled parts, and as a building block for compounded applications that require high flow and high stiffness.
Availability
North America
Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
65 g/10 min
Density (23 °C)
0.90 g/cm³
Flexural Modulus (0.05 in/min, 1% Secant, Procedure A)
290000 psi
Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A)
2000 MPa
Tensile Strength at Yield (2 in/min)
6100 psi
Tensile Strength at Yield (50 mm/min)
42 MPa
Tensile Elongation at Yield
6 %
Notched Izod Impact Strength (73 °F, Method A)
0.3 ft-lb/in
Notched Izod Impact Strength (23 °C, Method A)
16 J/m
Deflection Temperature Under Load (66 psi, Unannealed)
270 °F
Deflection Temperature Under Load (0.45 MPa, Unannealed)
132 °C