Description
Adsyl 7416 XCP is an advanced polyolefin selected by customers for use as a sealing layer in coextruded film applications. This grade features a low seal initiation temperature and good optics. It does not contain slip or anti-block additives.
Availability
Africa-Middle East, Asia-Pacific, Australia and New Zealand, Europe, North America, South & Central America
Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
7.5 g/10 min
Density (23 °C, Method A)
0.90 g/cm³
Tensile Stress at Yield
21 MPa
Flexural Modulus
600 MPa
Tensile Strain at Yield
14 %
Tensile Young's Modulus MD (50 µm, 25 mm/min)
290 MPa
Tensile Young's Modulus TD (50 µm, 25 mm/min)
320 MPa
Tensile Stress at Break MD (50 µm, 500 mm/min)
40 MPa
Tensile Stress at Break TD (50 µm, 500 mm/min)
42 MPa
Tensile Stress at Yield MD (50 µm, 500 mm/min)
15 MPa
Tensile Stress at Yield TD (50 µm, 500 mm/min)
15 MPa
Seal Initiation Temperature
115 °C
Vicat Softening Temperature (A50)
115 °C
Heat Deflection Temperature B (0.45 MPa, Unannealed)
52 °C
DSC Melting Point
133 °C
Haze (50 µm)
0.5 %
Gloss (45°, 50 µm)
90