Typical Properties
Melt Flow Rate (190 °C/2.16 kg)
19.5 g/10 min
Density (23 °C)
0.946 g/cm³
Flexural Young's Modulus
1201 MPa
Flexural Young's Modulus
174000 psi
Tensile Stress at Break (23 °C)
1920 psi
Tensile Stress at Break (23 °C)
13.2 MPa
Flexural Modulus (1% Secant)
146000 psi
Flexural Modulus (1% Secant)
1007 MPa
Flexural Modulus (2% Secant)
842 MPa
Flexural Modulus (2% Secant)
122000 psi
Tensile Elongation at Yield (23 °C)
12 %
Notched Izod Impact Strength (23 °C)
0.78 ft-lb/in
Notched Izod Impact Strength (23 °C)
41 J/m
Shore Hardness (Shore D, max)
64
Deflection Temperature Under Load (66 psi, Unannealed)
60 °C
Deflection Temperature Under Load (66 psi, Unannealed)
141 °F