Beon3D PP-GF-FR 2293G Natural is a glass fiber reinforced PP-based compound with a halogen-free flame retardant package targeting V-0 applications. This grade comes in a pellet form and is available in Black and Natural colors.
This formulation highlights low warpage, has a well-balanced mechanical performance, optimized surface quality, and features excellent dimensional accuracy while focusing on the ease of printability.
Beon3D grades are made to be used in various 3D printing processes and are available in natural and black colors.
The manufacturer of 3D-printed components is obligated to ensure that the used material and the applied manufacturing process meet the product-specific requirements and comply with the legal framework.
This material is not intended for use in in Medical, Pharmaceutical, Toys, Safety Components, Weapons, Cosmetic packaging, Food and Drinking Water applications.
BEON3D PP-GF-FR 2293G NATURAL
Description
Availability
Europe, North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Volume Flow Rate (230 °C/2.16 kg) | 4 cm³/10 min |
| Density | 1.16 g/cm³ |
| Flexural Modulus (23 °C) | 2700 MPa |
| Flexural Strength (23 °C) | 51 MPa |
| Tensile Modulus (23 °C) | 3200 MPa |
| Tensile Stress at Yield (23 °C) | 36 MPa |
| Tensile Elongation at Break (23 °C) | >=10 % |
| Charpy Impact Strength - Notched (23 °C) | 21 kJ/m² |
| Shore Hardness (Shore D, 1 sec) | 24 |
| Shore Hardness (Shore D, 15 sec) | 22 |
| Heat Deflection Temperature A (1.80 MPa, Unannealed) | 80 °C |
| Heat Deflection Temperature B (0.45 MPa, Unannealed) | 100 °C |
| Tensile Modulus (23°C) 0° | 3000 MPa |
| Tensile Modulus (23°C) 45° | 1200 MPa |
| Tensile Modulus (23°C) 90° | 1000 MPa |
| Tensile Modulus (23°C) Z | 600 MPa |
| Tensile Strength at Yield (23°C) 0° | 30 MPa |
| Tensile Strength at Yield (23°C) 45° | 16 MPa |
| Tensile Strength at Yield (23°C) 90° | 13 MPa |
| Tensile Strength at Yield (23°C) Z | 5 MPa |
| Tensile Elongation at Break (23°C) 0° | 7 % |
| Tensile Elongation at Break (23°C) 45° | 15 % |
| Tensile Elongation at Break (23°C) 90° | 9 % |
| Tensile Elongation at Break (23°C) Z | 5 % |
| Charpy Impact Strength - Notched (23°C) 0° | 35 kJ/m² |
| Charpy Impact Strength - Notched (23°C) 45° | 25 kJ/m² |
| Charpy Impact Strength - Notched (23°C) 90° | 20 kJ/m² |
| Charpy Impact Strength - Notched (23°C) Z | 7 kJ/m² |
| Flexural Modulus (23°C) 0° | 2800 MPa |
| Flexural Modulus (23°C) 45° | 1100 MPa |
| Flexural Modulus (23°C) 90° | 1000 MPa |
| Flexural Modulus (23°C) Z | 400 MPa |
| Flexural Strength (23°C) 0° | 31 MPa |
| Flexural Strength (23°C) 45° | 16 MPa |
| Flexural Strength (23°C) 90° | 14 MPa |
| Flexural Strength (23°C) Z | 7 MPa |
Process
3D Printing (Granules)
Resin
Polypropylene Compounds