CIRCULENRECOVER EP PA6 GF 15H BLACK is a 15% glass fiber reinforced, heat stabilized Polyamide 6 formulated on mechanical recycled sourcing. Standard color is black, color matching for dark colors possible. Automotive structural applications are possible. Sustainability: According with the requirements of Standard ISO 14021:2016, Circulen Recover EP PA6 GF15 H BLACK contains 55 % of recycled material that is fully based on pre-consumer waste. Recycled content according to DIN SPEC 91446:2021-12: R60 Data Quality Level according to DIN SPEC 91446:2021-12: DQL4 Data Quality Level according to VDA 284: DQL Automotive
CIRCULENRECOVER EP PA6 GF 15H BLACK
Description
Availability
Europe, Latin America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Density (Method A) | 1.24 g/cm³ |
| Apparent (Bulk) Density | 0.60 to 0.80 g/cm³ |
| Tensile Modulus (1 mm/min, Type 1A) | 5500 MPa |
| Tensile Stress at Break (Type 1A, 5 mm/min) | 115 MPa |
| Tensile Strain at Break (Type 1A, 5 mm/min) | 2.8 % |
| Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A) | 5.0 kJ/m² |
| Charpy Impact Strength - Unnotched (23 °C, Type 1, Edgewise) | 35 kJ/m² |
| Deflection Temperature Under Load Unannealed (0.45 MPa) (Flatwise) | 210 °C |
| Deflection Temperature Under Load Unannealed (1.80 MPa) (Flatwise) | 200 °C |
| Burning Rate (FMVSS 302) | <100 mm/min |
| Drying Time | 3.0 to 4.0 hr |
| Drying Temperature | 80 °C |
| Suggested Max Moisture | 0.040 to 0.10 % |
| Processing (Melt) Temp | 250 to 280 °C |
| Mold Temperature | 60 to 100 °C |