Hostacom TRG 436P NAT



Hostacom TRG 436P NAT is a glass fiber reinforced impact modified PP  with medium melt flow rate. It combines a well-balanced impact/stiffness ratio with good surface and high UV stability for applications requiring high ductility also at low temperatures.




SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin

Product Data and Technical Information

Typical Properties

Melt Flow Rate (230 °C/2.16 kg) 13 g/10 min
Melt Volume Flow Rate (230 °C/2.16 kg) 13 cm³/10 min
Density (23 °C) 1.21 g/cm³
Flexural Modulus (23 °C, Tech. A) 7500 MPa
Tensile Modulus (23 °C) 8000 MPa
Tensile Stress at Yield (23 °C) 85 MPa
Tensile Strain at Yield (23 °C) 3 %
Charpy Impact Strength - Notched (23 °C) 12 kJ/m²
Charpy Impact Strength - Notched (0 °C) 10 kJ/m²
Charpy Impact Strength - Notched (-30 °C) 10 kJ/m²
Charpy Impact Strength - Unnotched (23 °C) 55 kJ/m²
Charpy Impact Strength - Unnotched (0 °C) 55 kJ/m²
Vicat Softening Temperature (B50) 110 °C
Deflection Temperature Under Load (1.80 MPa, Unannealed) 140 °C

Technical Data Sheet

Technical Data Sheet


Injection Molding


Polypropylene Compounds


Exterior Automotive Applications, Outdoor and Power Tools

Prohibited Applications of Compounded Polyolefins:

The following applications and/or end uses are prohibited by LyondellBasell.  LyondellBasell will not solicit the sale of, or knowingly supply, product for use in the following applications:

FDA Class III medical devices, European Class III medical devices, Health Canada Class IV Medical Devices, applications involving permanent implantation into the body & life-sustaining medical applications